IML Injection Moulding Films 6

Applications

Specifi cally developed for in mould labels for PP and PE injection moulding.

Description

EUH is a white voided OPP film, matt on one side. Its special formulation results in a film with very high yield. The fi lm is treated on both sides. EUH is wound print side outside.

Product Features

• One side glossy, one side matt
• Suitable for sheet fed operations
• Good machineability and antistatic properties
• Very high yield due to very low density
• Soft touch effect after moulding
• Distortion free decoration
• Off set sheet fed printing with UV curing and oxidative drying inks. For off set printing the film should be stored at 20-25°C, 60-70% rh for a min. of 48 hours
• Gravure, UV-flexo printing
• For reel to reel printing with UV inks, inline Corona treatment is strongly recommended
• Screen printing and letterpress using UV inks
• Density (g/cm³): 0.55
• Nominal thickness (μm): 40 | 60 | 70 | 75
• Unit weight (g/m²): 22.0 | 33.0 | 38.5 | 41.3
• Average yield (m²/kg): 45.5 | 30.3 | 26.0 | 24.2

Applications

Specifically developed for in mould labels for PP and PE injection moulding.

Description

EUP is a white voided OPP film, matt on both sides. The unique product design is leading to superior converting characteristics and its special formulation results in a film with very high yield. EUP is normally wound print side outside.

Product Features

• Improved sheet fed performance
• Excellent machineability and antistatic properties
• Very high yield due to very low density
• Soft touch effect after moulding
• Distortion free decoration
• Offset sheet fed printing with UV curing the film should be stored at 20-25°C, 60-70% rh for a min. of 48 hours
• Gravure and UV-flexo printing
• For reel to reel printing with UV inks, inline Corona treatment is strongly recommended
• Screen printing and letterpress using UV inks
• Density (g/cm³): 0.55
• Nominal thickness (μm): 50 | 60 | 70
• Unit weight (g/m²): 27.5 | 33.0 | 38.5
• Average yield (m²/kg): 36.4 | 30.3 | 26.0

Applications

Developed for in mould labels for PP and PE injection moulding.

Description

ELR70 is a white voided OPP film, specifically developed for label applications where the conversion of large sheets and finally large labels is required. ELR70 is treated on both sides, one side is matt, one side is glossy.

Product Features

• Excellent antistatic properties
• Superior machineability and die cutting
• Good web flatness
• Suitable for sheet fed operations
• Improved yield due to low density
• Glossy effect after injection moulding
• Offset sheet fed printing with UV curing and oxidative drying inks. For offset printing the film should be stored at 20-25°C, 60-70% rh for a min. of 48 hours
• Gravure and UV-flexo printing
• For reel to reel printing with UV inks, inline Corona treatment is strongly recommended
• Screen printing and letterpress using UV inks
• Density (g/cm³): 0.88
• Nominal thickness (μm): 70
• Unit weight (g/m²): 59.8
• Average yield (m²/kg): 16.7

 

Applications

Specifically developed for in mould labels for PP and PE injection moulding.

Description

EWR is a white OPP film, treated on both sides, one side is matt, one side glossy.

Product Features

• Good antistatic properties, web flatness and machineability
• Offset sheet fed printing with UV curing and oxidative drying inks. For offset printing the film should be stored at 20-25°C, 60-70% rh for a min. of 48 hours.
• Gravure and UV-flexo printing
• For reel to reel printing with UV inks, inline Corona treatment is strongly recommended
• Screen printing and letterpress using UV inks
• Density (g/cm³): 0.96
• Nominal thickness (μm): 50 | 57
• Unit weight (g/m²): 48.0 | 54.7
• Average yield (m²/kg): 20.8 | 18.3

Applications

Specifically developed for in mould labels for PP and PE injection moulding.

Description

ETH is a transparent OPP film, treated and glossy on both sides.

Product Features

• Good antistatic properties, web flatness and machineability
• Offset sheet fed printing with UV curing and oxidative drying inks. For offset printing the film should be stored at 20-25°C, 60-70% rh for a min. of 48 hours.
• Gravure and UV-flexo printing
• For reel to reel printing with UV inks, inline Corona treatment is strongly recommended
• Screen printing and letterpress using UV inks
• Density (g/cm³): 0.91
• Nominal thickness (μm): 50 | 57
• Unit weight (g/m²): 45.5 | 51.9
• Average yield (m²/kg): 22.0 | 19.3

Applications

Specifically developed for in mould labels for PP and PE injection moulding.

Description

ETR is a matt, transparent OPP film. ETR is treated on both sides, one side matt and one side glossy.

Product Features

• Good antistatic properties, web flatness and machineability
• Offset sheet fed printing with UV curing and oxidative drying inks. For offset printing the film should be stored at 20-25°C, 60-70% rh for a min. of 48 hours.
• Gravure and UV-flexo printing
• For reel to reel printing with UV inks, inline Corona treatment is strongly recommended
• Screen printing and letterpress using UV inks
• Density (g/cm³): 0.91
• Nominal thickness (μm): 57
• Unit weight (g/m²): 51.9
• Average yield (m²/kg): 19.3