WAL Cut & Stack Films 5

Treofan WAL cut & stack films are designed to match the specific requirements of this specialised segment – such as superior de-stacking and antistatic properties.

LUH White Voided WAL - Cut & Stack Film

  • Treated glossy surface
  • White OPP layer
  • Highly voided OPP core
  • OPP layer
  • Treated matt surface

Get Further Information

Applications

Specifically developed for self adhesive face stock and cut & stack wrap around labels.

Description

LUH is a white voided OPP film, matt on one side. Its special formulation results in a film with very high yield. The film is treated on both sides. LUH 40 has been designed for reel fed, all other thicknesses for cut & stack applications. LUH is wound print side outside.

Product Features

  • Suitable for sheet fed operations
  • Good machineability and antistatic properties
  • Very high yield due to very low density
  • Soft touch effect after moulding
  • Distortion free decoration
  • Offset sheet fed printing with UV curing and oxidative drying inks. For offset printing the film should be stored at 20-25°C, 60-70% rh for a min. of 48 hours
  • Gravure, UV-flexo printing
  • For reel to reel printing with UV inks, inline Corona treatment is strongly recommended
  • Screen printing and letterpress using UV inks
  • Density (g/cm³): 0.55
  • Nominal thickness (μm): 60 | 70 | 75
  • Unit weight (g/m²): 33.0 | 38.5 | 41.3
  • Average yield (m²/kg): 30.3 | 26.0 | 24.2

ELR White Voided WAL - Cut & Stack Film

  • Treated glossy surface
  • OPP layer
  • Voided OPP core
  • OPP layer
  • Treated matt surface

Get Further Information

Applications

Specifically developed for cut & stack wrap around labels.

Description

ELR70 is a white voided OPP film, specifically developed for label applications where the conversion of large sheets and finally large labels is required. ELR70 is treated on both sides, one side is matt, one side is glossy.

Product Features

  • Excellent antistatic properties
  • Superior machineability and die cutting
  • Good web flatness
  • Suitable for sheet fed operations
  • Improved yield due to low density
  • Glossy effect after injection moulding
  • Offset sheet fed printing with UV curing and oxidative drying inks. For offset printing the film should be stored at 20-25°C, 60-70% rh for a min. of 48 hours
  • Gravure and UV-flexo printing
  • For reel to reel printing with UV inks, inline Corona treatment is strongly recommended
  • Screen printing and letterpress using UV inks
  • Density (g/cm³): 0.88
  • Nominal thickness (μm): 70
  • Unit weight (g/m²): 59.8
  • Average yield (m²/kg): 16.7

LPT Thick Solid - Transparent WAL Cut & Stack Film

  • Treated high gloss surface
  • Transparent OPP core
  • Treated high gloss surface

Get Further Information

Applications

Specifically developed for cut & stack wrap around labels.

Description

LPT is a treated transparent OPP film, treated and glossy on both sides.

Product Features

  • Good antistatic properties, web flatness and machineability
  • Offset sheet fed printing with UV curing and oxidative drying inks. For offset printing the film should be stored at 20-25°C, 60-70% rh for a min. of 48 hours.
  • Gravure and UV-flexo printing
  • For reel to reel printing with UV inks, inline Corona treatment is strongly recommended
  • Screen printing and letterpress using UV inks
  • Density (g/cm³): 0.91
  • Nominal thickness (μm): 57
  • Unit weight (g/m²): 51.9
  • Average yield (m²/kg): 19.3

LPR Thick Solid - Transparent SAL - Face Stock Film

  • Treated glossy surface
  • OPP layer
  • Transparent OPP core
  • OPP layer
  • Treated matt surface

Get Further Information

Applications

Specifically developed for cut & stack wrap around labels.

Description

LPR is a matt, transparent OPP film. LPR is treated on both sides, one side matt and one side glossy.

Product Features

  • Good antistatic properties, web flatness and machineability
  • Offset sheet fed printing with UV curing and oxidative drying inks. For offset printing the film should be stored at 20-25°C, 60-70% rh for a min. of 48 hours.
  • Gravure and UV-flexo printing
  • For reel to reel printing with UV inks, inline Corona treatment is strongly recommended
  • Screen printing and letterpress using UV inks
  • Density (g/cm³): 0.91
  • Nominal thickness (μm): 57
  • Unit weight (g/m²): 51.9
  • Average yield (m²/kg): 19.3

LPW Thick Solid - Solid White WAL Cut & Stack Film

  • Treated glossy surface
  • OPP layer
  • White OPP core
  • Treated matt surface

Get Further Information

Applications

Specifically developed for cut & stack wrap around labels.

Description

LPW is a white OPP film, treated on both sides, one side is matt, one side glossy.

Product Features

  • Good antistatic properties, web flatness and machineability
  • Offset sheet fed printing with UV curing and oxidative drying inks. For offset printing the film should be stored at 20-25°C, 60-70% rh for a min. of 48 hours.
  • Gravure and UV-flexo printing
  • For reel to reel printing with UV inks, inline Corona treatment is strongly recommended
  • Screen printing and letterpress using UV inks
  • Density (g/cm³): 0.96
  • Nominal thickness (μm): 57
  • Unit weight (g/m²): 54.7
  • Average yield (m²/kg): 18.3